Ceramic Fibre Paper
- Color: White
- Fiberfrax Product Properties: Ceramic Fibre Paper
- Maximum Temp.degreeC: 1260
- Dimensions (mm): 1000x1000
- Thickness (mm): 1 - 6
- Application Area: Combustion chamber Lining,Back up insulation,Expansion joints,Wrapping etc.
We are involved in offering a wide range of Ceramic Fibre Paper. These products are light weight refractory material processed from a blend of high purity alumina - silica fibres into a highly flexible, uniform sheet.
Ceramic Fibre Blankets
- Usage/Application: Industrial
- Thickness: 10 to 50mm
- Brand: Caldery's
- Fiberfrax Product Properties: Blankets,Durablanket Z,Durablanket S
- Maximum Use/Grade Temp., C: 1425,1260
- Thickness, Mm Density, Kg/M3 (Lbs/Cutt): 6,96,13,25,128 & 160 (4,19,38 & 50 64,8 & 10)
We offer ceramic fiber blankets, which is made of special ceramic long-fiber that is produced by the melting of very pure raw materials in double surface meeting process with out binders and with good stability in a large range of temperature. The process of double surface needling increase interweaving and tensile strength. Its unique fiber layup and needling process provide ceramic fiber blanket with outstanding consistency, handling strength and resiliency at elevated temperatures.
Light Resins Bonded Mattresses LRB
- Thickness: 25mm to 100mm
- Brand: SKG
- Density (kg/cu.m.): 100,120,150
- Metal Facing: G.I. Hexogonal wire netting 3/4" x 24G
- Size of mattresses: 1640mm x 1220mm
- Maximum Service Temperature: 750degreeC
Minrock Rockwool lightly bonded mattresses (LRB) consist of fine fibres spun 1 from selected rocks melted at a high temperature and bonded with a thermosetting resin. They are then felted in the predetermined fibre lay pattern and are baked to form preformed mattress of predetermined density and thickness with uniform fibre distribution.
Thermal ConductivityMinrock products have extremely low K-values for the wide range of temperatures. Typical thermal conductivity values for various densities and mean temperatures are given in the graph.
Compression ResistanceMinrock mattresses offer high resistance to compression. Minrock LRB mattresses regain their nominal thickness after removal of a normal compressive load.
Moisture ResistanceMinrock Rockwool mattresses are water repellant and do not absorb moisture by capillary action or ambient moisture from the atmosphere. Should blankets become wet, full thermal efficiency will be restored after drying out the moisture.
Corrosion Resistance Minrock mattresses do not cause, initiate or promote corrosion.
FlexibilityMinrock mattresses are designed for maximum flexibility. They will essentially retain their thickness while conforming to virtually any irregular shape. Retention of fibres by the wire prevents any cracking or breaking.
Fire ResistanceMinrock mattresses are incombustible and resist the spread of flames.
Ceramic Fibre Products
- Resistance Durability: Fire Resistant,Heat Resistant
- Brand: SKG
- Condition: New
- B.D. Gm/cc: 3
- Block Size (mm): 600 x 300 x 115 600 x 300 x 150
- PLC (1550degreeC/3 hrs): 1.46
- Porosity (Vol%): 16.5-17.0
We are engaged in presenting a stunning range of PCPF Blocks. Our experts are using superior quality material and cutting edge technology to offer these PCPF Blocks.
Ceramic Fibre Board
- Thickness: 12/13, 25, 38 & 50
- Fiberfrax Product Properties: Ceramic Fibre Board
- Maximum Temp.degreeC Grade: 1600,1425, 1260 Cervac - 80, Cervac - Z, Cervac - HS, Cervac - HD
- Dimensions (mm): 500x1000
- Thermal Conductivity at min temp.: 0.11 - 0.13
- Density (Kg/m): 320 , 416,480,576 & 640
Designed with perfection, we are engaged in presenting a wide assortment of Ceramic Fibre Boards.
Calcium Silicate Blocks
- Cement Industry: Preheater cyclones,precalcinator,klin riser duct
- Sugar: Boiler,Steam & Process Pipeline
- Application: Floors & Roofs
- Structurally Insulated: Yes
- Power Plants: Boilers,steam pipelines,exhaust ducts of gas based plants
- Fertilizer, Refinery & Petrochemical Industry: Reformer,gas cracker,heater,ducts,boiler
We are channel partners for Hysil Calcium Silicate Blocks. The raw materials for calcium silicate bricks include lime mixed with quartz, crushed flint or crushed siliceous rock together with mineral colorants. The materials are mixed and left until the lime is completely hydrated, the mixture is then pressed into molds and cured in an autoclave for two or three hours to speed the chemical hardening.
Products Overview:
Physical PropertiesProduct | Size Mm | Thickness Mm | BD Kg/M2 | Flexural Strength Mpa | Temp °C |
Calcium Silicate Blocks | 900 X 600 600 X 150 | 25-100 25-100 | 250 250 | 0.87-0.90 0.87-0.90 | 800 / 1000 / 1100 800 / 1000 / 1100 |
Rigid Pipe Covering | 900/ 600/ 450 | 25-75 | 250 | 0.8-0.9 | 800 / 1000 / 1100 |
Chemical CompositionCharacteristics | H-800 Grade | Values % H-1000 Grade | H-1100 Grade |
SiO2 | 40-44 | 42-46 | 44-48 |
CaO | 34-38 | 34-38 | 35-38 |
AI2O3 | 3.2-4.5 | 3.2-4.5 | 3.5-4.5 |
Fe2O3 | -0.7 | ~0.7 | ~0.7 |
MgO | ~1.3 | ~1.3 | ~1.3 |
LOI | <15 At 800°C | <14 At 950°C | <11 At 1025°C |
Ceramic Fibre Modules
- Maximum Use/Grade Temp., degreeC: 1450,1300
- Thermal Conductivity At Min Temp.: 0.12 (0.84) For 160 Kg/M3
- Fiberfrax Product Properties: Properties Modules Z,S A B Anchored Cerlock Cermax
Our company is involved in producing ceramic fiber modules. This module contains no binders. We use special equipment for producing ceramic fiber module to confirm the precise dimensions. Ceramic fiber module can be connected with structures of kiln and furnace by the anchor. It’s easy to install and speed constructing lining of the furnace.